DAMAGE OF THE CuPb20 SLIDING BEARING
Authors:
Jan Luštinec1
, Vladivoj Očenášek1, Jan Kec1
1SVÚM a.s., Czech Republic
Received 23 February 2017
Accepted 20 March 2017
Available 30 March 2017
Abstract:
The analysis of hydrodynamic steel sliding bearing with leaded bronze lining, which had a reduced shortened lifetime due to its unequal wear, was carried out. The lining structure of this bearing was compared to those of the bearing with a high lifetime and of the unused bearing. It was shown that the short lifetime is caused by wrong lubricating oil. The use of unsuitable oil led to the formation of hard and brittle layer containing phosphide (Cu3P) at the lining surface. The scaling off particles of the layer influenced the friction conditions and accelerated the wear.
Keywords:
Sliding bearing, Cu-Pb lining, damage, dendritic structure
References:
[1] J. Priester, Klzné ložiská, Alfa, Bratislava – Praha, 1981.
[2] F. Boháček, Části a mechanismy strojů II: Hřídele, tribology, ložiska, Ediční středisko Vysokého učení technického, Brno, 1987.
[3] J. Pluhař, Nauka o materiálech, Nakladatelství technické literatury, Praha, 1989.
[4] J. Pluhař, J. Koritta, Strojírenské materiály, Nakladatelství technické literatury, Praha, 1977.
[5] F. Píšek, L. Jeníček, P. Ryš, Nauka o materiálu I-3 Neželezné kovy, Nakladatelství ČSAV, Praha, 1973.
[6] J.P. Pathak, S.N. Tiwari, On the mechanical and wear properties of copper-lead bearing alloys, Wear, 155 (1), 1992: pp.34-47.
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License (CC BY-NC 4.0)
Volume 9
Number 3
September 2024
Last Edition
Volume 9
Number 3
September 2024
How to Cite
J. Luštinec, V. Očenášek, J. Kec. Damage of the CuPb20 Sliding Bearing. Applied Engineering Letters, 2(1), 2017: 16-21.
More Citation Formats
Luštinec, J., Očenášek, V., & Kec. J. (2017). Damage of the CuPb20 Sliding Bearing. Applied Engineering Letters, 2(1), 16-21.
Luštinec, Jan, et al. “Damage of the CuPb20 Sliding Bearing.“ Applied Engineering Letters, vol. 2, no. 1, 2017, pp. 16-21.
Luštinec, Jan, Vladivoj Očenášek, and Jan Kec. 2017. “Damage of the CuPb20 Sliding Bearing.“ Applied Engineering Letters, 2 (1): 16-21.
Luštinec, J., Očenášek, V. and Kec. J. (2017). Damage of the CuPb20 Sliding Bearing. Applied Engineering Letters, 2(1), pp. 16-21.
Journal Menu
Archive
DAMAGE OF THE CuPb20 SLIDING BEARING
Authors:
Jan Luštinec1
, Vladivoj Očenášek1, Jan Kec1
1SVÚM a.s., Czech Republic
Received 23.02.2017.
Accepted 20.03.2017.
Available 30.03.2017.
Abstract:
The analysis of hydrodynamic steel sliding bearing with leaded bronze lining, which had a reduced shortened lifetime due to its unequal wear, was carried out. The lining structure of this bearing was compared to those of the bearing with a high lifetime and of the unused bearing. It was shown that the short lifetime is caused by wrong lubricating oil. The use of unsuitable oil led to the formation of hard and brittle layer containing phosphide (Cu3P) at the lining surface. The scaling off particles of the layer influenced the friction conditions and accelerated the wear.
Keywords:
Sliding bearing, Cu-Pb lining, damage, dendritic structure
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License (CC BY-NC 4.0)
Volume 9
Number 3
September 2024
Last Edition
Volume 9
Number 3
September 2024